Iron Scale Use For Extracting Reduced Iron Powder
Click:217 Date:2016/6/24 16:22:14

 Reduction of iron scale manufacturing production processes generally divided into coarse

 and fine reduction reduction. The iron scale at about 1100 ℃ coarsely restore process to

 restore w (Fe> 95%, w (C <0.5% of the sponge iron ;then pulverizing the resulting block 

of sponge iron at a temperature of 800 ~ 1000 ℃ in in an atmosphere of pure hydrogen or

 ammonia decomposition , for fine reduction . Finally, pulverized and sieved to adjust the 

particle size ,made of iron .
   Containing iron sclale is reduced to w ( more Fe98% of sponge iron by slag , crushing, 

magnetic separation after screening , for fine reduction, reduced iron production of qualified 

and then finely ground into the mill by grading

sieve to get different granularity of high purity iron . finer granularity of the key components

for the production of iron equipment , just die , to a molding, high strength , wear-resistant , corrosion-resistant parts , can be used in the defense industry, aerospace manufacturing , 

transportation , oil exploration and ther important industries. coarser iron powder can be used in the production of welding 

electrodes .

1. is used as the raw material of iron or steel sintering aid to help melt slag agent.
FeO content in the iron scale up to more than 50 %, which is better assisted sintering iron-containing materials , theoretical results show that , 1kg FeO exothermic oxidation of Fe2O3

to 1973 joules. After sintering the mix with added iron skin, due to the high temperature 

sintering process fully , so sintering productivity ,solid fuel consumption down . Production 

practice shows that 8% of the oxide scale can yield about 2%. Our company tai’an shuoyun 

chemical  use of iron sacle as an auxiliary material, mix with addition of iron ore in the skin,

 on the one hand , due to the relatively large iron oxide particle to improve the permeability of

 the sinter bed ; hand, iron scale during sintering heat thereby reducing the consumption of 

solid fuel .
In addition . The use of iron sacle can be used as a flux for fluxing ore , used in steelmaking . 

Co- melting of iron scale is used as slag-forming agent is a highly efficient smelting fluxing material steel to improve efficiency and

reduce coke,coal consumption and prolong the life of the converter furnace .
2.  Alternative smelting ferrosilicon alloy steel scrap or scrap substitute for steelmaking furnace . 

Smelting ferrosilicon alloy steel scrap is an important raw material for the smelting of ferroalloys

annual cuttings about 2 million tons of steel , and the steel industry waste each year about 10

million tons of iron

scale. Alternative has been developed with the iron scale silicon alloy steel scrap smelting of 

new  technology, and achieved good economic results.
EAF requires scrap as raw material, scrap steel material for more stringent requirements , but

such a small number of scrap steel , high prices , lack of supply. At low prices and a wide 

range  of sources of iron oxide ,steel slag and other waste as the main raw material , replace

the less high prices of scrap , with significant economic benefits.

 
Links: Facebook  |   ECVV  |  
  
ShuoYun CMS Enterprise Web Site Management System All rights reserved 鲁ICP备12118166号
  
Add:NO.1 Building West,NO.32 Dongyue Road,Taishan District,Tai'an city,Shandong Province,China
  
Tel:+86-538-6632037   Fax:+86-538-8939927  E-mail:sychems@hotmail.com